The ammonia concentration is prepared for PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC
Время: 2024-02-04

magnetic separator for sale

Solution a with a metal ion concentration of 100g/l was prepared by nickel sulfate, manganese sulfate and ferrous sulfate heptahydrate according to the molar ratio of ni, mn and fe at 6:2:2. At 380rpm and 55℃, 28% ammonia solution (solution b) and 18% sodium hydroxide solution (solution c) were added. For PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC, a substrate with an ammonia concentration of 5g/l and a ph of 11.6 was prepared.

PTMS Electromagnetic Separator

Solution a, b and c were added into PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC magnetic reactor at a flow rate of 8l/h, 0.9l/h and 2.55l/h, respectively. The ph of the reaction system was controlled to be 10.5, and the coprecipitation reaction was carried out. When the solution reached 7μm, After washing, filtration and drying, the precursor with specific surface area of 14m2/g and solid density of 1.8g/cm3 was obtained

what is magnetic separation?

With lithium carbonate, sodium carbonate according to lithium, sodium and transition metal molar ratio 0.4:0.6: 1.0 After mixing evenly, heating at 4℃/min to 450℃ for 5h, and then heating at 3℃/min to 750℃ for 12h, PTMS LITHIUM COBALT ACID MATERIAL MAGNETIC field obtained positive electrode material.

Contact: DELLA

Mob: +86-13929907491


Подписаться на новости

Foshan Powtech Technology Company Limited.

Адрес : No.9, Factory 2, Shijin Industry Park, Shishan Town, Nanhai District, Foshan City, Guangdong, China

Тел. : +86 -13929907491

Эл. адрес : sales@ptmsmagnet.com

Веб-сайт : https://www.dellamagnet.com

Авторское право © Foshan Powtech Technology Company Limited. Сохранить все права.   Sitemap   XML